1050 1060 1100 Aluminum Plate /Sheet
Product
- Stainless Steel
- Stainless Steel Sheet/Plate Stainless Steel Coil Stainless Steel Tube/Pipe Stainless Steel Bar Stainless Steel Wire
- Carbon Steel
- Carbon Steel Sheet/Plate Carbon Steel Tube/Pipe Carbon Steel Coil Carbon Steel Bar Bulb Flat Bar Weathering Steel Wear Plate Silicon Steel Coil
- Galvanized Steel
- Galvanized Steel Sheet/Plate Galvanized Steel Coil Galvanized Steel Tube/Pipe Galvanized Steel Wire PPGI Coil
- Aluminum
- Aluminum Coil/Strip Aluminum Sheet/Plate Aluminum Tube/Pipe Aluminum Bar/Rod Aluminum Circle/Wafer Aluminum Wire Aluminum Profile
Aluminum Sheet/Plate
5005 5052 Aluminum Plate / Sheet
Product Introduction
| Technical Parameters of Aluminum Sheet/Plate | |||
| Parameter Category | Specific Parameter | Description / Typical Values | Common Standards (Examples) |
| Basic Identification | Alloy Designation | A numerical code indicating the chemical composition. Common Alloys: 1100, 3003, 5052, 6061, 7075 | ASTM B209, AMS-QQ-A-250 |
| Temper | A designation indicating the mechanical strength and hardness achieved by heat treatment or work hardening. Common Tempers: O (Annealed), H14 (1/4 Hard), H32 (Strain Hardened & Stabilized), T6 (Solution Heat Treated & Artificially Aged) | ASTM B209, AMS-QQ-A-250 | |
| Dimensional Specifications | Thickness | Range: 0.2 mm to 150+ mm Common Units: mm, inches (in or "), BWG (Birmingham Wire Gauge) for thinner sheets. | / |
| Width | Range: 500 mm to 2500+ mm (depending on mill capacity) | / | |
| Length | Range: 1000 mm to 12000+ mm (depending on mill capacity) | / | |
| Tolerances | Standard tolerances for thickness, width, and length as per relevant standards. (e.g., ± 0.10mm for thickness | ASTM B209 | |
| Mechanical Properties | Ultimate Tensile Strength (UTS) | The maximum stress the material can withstand while being stretched. Example (6061-T6): 45 ksi (310 MPa) | ASTM E8/E8M |
| Tensile Yield Strength (TYS) | The stress at which the material begins to deform plastically. Example (6061-T6): 40 ksi (276 MPa) | ASTM E8/E8M | |
| Elongation at Break | The degree to which the material can be plastically deformed before fracture, expressed as a percentage. Example (6061-T6): 8-12% | ASTM E8/E8M | |
| Hardness | Resistance to indentation. Common Scales: Brinell (HB), Rockwell (B & E scales for Al). Example (6061-T6): Rockwell B 60 | ASTM E10, E18 | |
| Physical Properties | Density | Typical Value: 2.70 g/cm³ (0.098 lb/in³) | / |
| Melting Point | Approximate Range: 600°C - 660°C (1112°F - 1220°F), depending on alloy. | / | |
| Electrical Conductivity | Expressed as a percentage of International Annealed Copper Standard (IACS). Example (1100-O): 59% IACS | ASTM B193 | |
| Thermal Conductivity | Typical Range: 120 - 240 W/m·K | ASTM E1461 | |
| Chemical Composition | Aluminum (Al) Content | Base metal, typically 85% to 99+%. | / |
| Major Alloying Elements | Elements added to achieve specific properties. Examples: • 1xxx: 99%+ Al • 3xxx: Manganese (Mn) • 5xxx: Magnesium (Mg) • 6xxx: Magnesium & Silicon (Mg & Si) • 7xxx: Zinc (Zn) | ASTM B209, EN 573 | |
| Surface Characteristics | Surface Finish | Standard Mill Finishes: • Mill Finish (unfinished) • Embossed (patterned) • Anodized (decorative or hardcoat) • Painted/Coated (PVDF, Polyester) | / |
| Surface Flatness | Tolerance for deviation from a flat plane. | / | |
| Thermal Treatment | Thermal Conductivity | (See under Physical Properties) | / |
| Coefficient of Thermal Expansion (CTE) | Typical Value: ~23 x 10⁻⁶ /°C (at 20°C) | ASTM E228 | |
| Standard Specifications | Quality & Testing Standards | Documents governing the material's production, testing, and acceptance. Examples: ASTM B209, ASME SB-209, AMS 4037, EN 485 | (Listed in adjacent column) |
Online message
- Prev： No Prev
- Next： 6082 Aluminum Plate
Have Any Questions?
DON'T HESITATE TO CONTACT US ANY TIME.